Propiedades mecánicas
Brass has different mechanical properties due to different zinc content. Fig. 7 is a graph showing the change of mechanical properties of brass with different zinc content. For brass, σb and δ increase with the increase of zinc content. For ( plus ) brass, the strength at room temperature increases continuously before the zinc content increases to about 45 percent . If the zinc content is further increased, the R phase with greater brittleness (solid solution based on Cu5Zn8 compound) appears in the alloy structure, and the strength decreases sharply. The room temperature plasticity of ( plus ) brass always decreases with the increase of zinc content. Therefore, the copper-zinc alloy containing more than 45 percent zinc has no practical value.
El latón común es ampliamente utilizado, como la correa del tanque de agua, el suministro de agua y la tubería de drenaje, la medalla, la tubería corrugada, la tubería serpentina, la tubería del condensador, la carcasa de la carcasa, varios productos perforados complejos, hardware, etc. Con el aumento del contenido de zinc de H63 a H59, pueden resistir bien el procesamiento en caliente y se utilizan principalmente en diversas partes de maquinaria y aparatos eléctricos, piezas de estampado e instrumentos musicales.
Para mejorar la resistencia a la corrosión, la fuerza, la dureza y la maquinabilidad del latón, una pequeña cantidad de elementos como estaño, aluminio, manganeso, hierro, silicio, níquel, plomo, etc. (generalmente 1 por ciento 2 por ciento, algunos hasta 3 por ciento 4 por ciento , y algunos hasta 5 por ciento ) se agregan a la aleación de cobre-zinc para formar aleaciones ternarias, cuaternarias o incluso quinarias, que son complejas
Coeficiente equivalente de zinc
The microstructure of complex brass can be calculated according to the "zinc equivalent coefficient" of elements added in brass. Because a small amount of other alloying elements are added to Cu-Zn alloy, the /( plus ) phase region in Cu-Zn state diagram usually moves to the left or right. Therefore, the microstructure of special brass is usually equivalent to that of ordinary brass with increased or decreased zinc content. For example, the microstructure of Cu-Zn alloy with 1 percent silicon is equivalent to the alloy structure with 10 percent zinc added in Cu-Zn alloy. So the "zinc equivalent" of silicon is 10. The "zinc equivalent coefficient" of silicon is the largest, which makes the /( plus ) phase boundary in Cu-Zn system significantly move to the copper side, that is, the phase region is strongly reduced. The "zinc equivalent coefficient" of nickel is negative, that is, the phase region is enlarged.
El -fase y -fase en latón especial son soluciones sólidas complejas de varios-elementos, que tienen un gran efecto de refuerzo, mientras que el -fase y -fase en el latón común son soluciones sólidas simples de Cu-Zn, que tienen un bajo efecto de refuerzo. Aunque el equivalente de zinc es equivalente, las propiedades de la solución sólida multicomponente y la solución sólida binaria simple son diferentes. Por lo tanto, una pequeña cantidad de refuerzo de -elementos múltiples es una forma de mejorar las propiedades de la aleación.